    Glass lined equipment is a kind of vessel which cylinder was made of high quality carbon steel lined with special silicate glass by fritting at a high temperature, with mechanical strength as steel vessel, anti-corrosive as glass equipment
    INQUIRY
    Description Enamel Characteristic Chemical Property Corrosive Allowance
    Introduction

    Glass lined equipment is a kind of vessel which cylinder was made of high quality carbon steel lined with special silicate glass by fritting at a high temperature, with mechanical strength as steel vessel, anti-corrosive as glass equipment, ideal multi-functional corrosive resistance equipment for hydrolysis, neutralization, crystallization, distillation, evaporation and stocking in pharmaceutical, chemical industries.
     

    Application

    Applied with high corrossive resistance characteristics technology glass lined reactor manufacture; this achieved the reactor with highly corrosion resistant, chemical inert, as ideal equipment for different processing environment, as below:
    pharmaceutical and veterinary drugs
    chemical and fine chemicals
    dyeing industry
    organic synthesis
    food-stuff industry



    Technical Parameter

     
    Volume Nominal Volume 50L ~5000L
    Total Volume 71L ~610L
    Design Temperature 0-180°C
    Heat Transfer Area 0.34~13.2 m2
    Design Pressure Cylinder Stuffing 0.2Mpa
    Mechanical Seal 0.4 Mpa
    Jacket 0.6 Mpa
    Agitating Speed Frame/Anchor 60 r/min
    Impeller/Paddle 130 r/min
    Motor & Reducer Motor Type Y100L2-4-B5
    Frame Type BLD22-23Q
    Impeller Type BLD22-11Q
    Motor Power 0.75~11kw
    Net Weight 480~4760 kgs


    Technical Drawing















     


















    Nozzle Dimension

     
    Model (L) Dimension Heating System Weight (Kg)
    D D1 D2 D3 D4 D5 D6 D7 N-φ       n-d       h1 h2 h3 h4 h Ventilator
    pipe
    Ventvalve
    BFK50 500 602 718 420 300 500 380 240 4-18     4-M16       400 280 850 300 1940 2-25 G1/2” 480
    BFK100 600 702 818 500 360 600 420 240 4-18 4-M20 550 315 850 320 2030 3-25 G1/2” 550
    BFK200 700 804 930 620 420 670 540 320 4-23 4-M20 700 334 913 420 2380 4-40 G1/2” 728
    BFK300 800 904 1032 703 480 760 600 320 4-23 4-M20 810 365 913 370 2503 4-40 G1/2” 1020
    BFK500 900 1004 1136 803 540 800 630 320 4-23 4-M20 980 395 945 400 2650 4-40 G1/2” 1247
    BFK1000 1200 1304 1480 1100 720 1100 840 320 4-30 4-M20 1200 470 1120 500 3205 4-50 G1/2” 1760
    BFK1500 1200 1304 1480 1100 720 1100 840 410 4-30 4-M20 1550 470 1120 500 3555 4-50 G1/2” 1940
    BFK2000 1400 1524 1700 1300 840 1300 1000 410 4-30 4-M20 1500 520 1149 490 3570 4-50 G1/2” 2334
    BFK3000 1600 1754 1934 1440 800 1228 1120 450 4-30 4-M20 1740 560 1300 600 4100 3-50 2-70 G1/2” 3205
    BFK5000 1750 1904 2440 1575 900   1200 500 4-30 4-M24 2280 610 1460 700 5100 3-70 2-80 G1/2” 4616
     
    Glass-Lined Enamel Characteristics

    We provided high content cobaltous oxide and silica anti-corrosive enamel for glass lined equipment, pipeline and fittings, which coating on the surface of metallic matrix and through high temperature 950℃~980℃ furnace for enamel firing, make the glass lined equipment have the performance of metal strength and glass material stabilities.
     

     Physical Property
    Test Item Results Standard
    Mechanical Impact resistance of glass-lined layer >220 x 10-3 J GB25025-2010
    Enamel Thickness (mm) 0.8~2.0mm GB25025-2010
    Preliminary Spark Test (V) 20kV GB25025-2010
    Final Spark Test(V) 7kV GB25025-2010
    Thermal/Cooling shock resistance of glass-lined layer (℃) Cooling Impact:
    Thermal Impact:

    110℃
    120℃
    GB25025-2010
    Design Temperature (℃) 0℃~180℃ GB25025-2010

    Glass Lined Reactor Chemical Property
    Glass Lined Equipment Enamel Chemical Resistance Allowance List

     

    No.

    Medium Name

    Concentration

    Temp.

    Corrosive Rate mm/y
    No.
    Medium

    Concentration

    Temp.

    Corrosive Rate mm/y
    1 HCL <35 <105 <0.005 22 Al2 (SO4)3 20-50 <105 <0.005
    2 HCL >5 >105 0.02-0.05 23 NH4 Cl <50 <105 <0.005
    3 HNO3 5-75 <105 <0.005 24 HCHO -100 <105 <0.005
    4 HNO3 100 <60 <0.005 25 K2 SO4 10 <105 <0.005
    5 H2SO4 <80 150 <0.005 26 NaCl 50 105 <0.005
    6 H3PO4 40 100 0.02-0.05 27 C2 H2O4 10 <38 <0.005
    7 H3PO4 40 >150 >0.05 28 NaF <5 <100 <0.005
    8 H3PO4 30-80 <100 <0.005 29 NaHSo 20-50 100 <0.02
    9 NaOH <25 Room Temp. <0.005 30 C2 H4 (NH2)OH -100 <105 <0.005
    10 NaOH 20 60 >0.02 31 C2 H4 (NH2)OH -100 <200 <0.005
    11 NaOH 20 80 >0.05 32 Br 100 <80 0.005-0.02
    12 NaOH 30 <38 <0.005 33 CCl 4 50-100 <105 <0.005
    13 Na2CO3 30 60 <0.03 34 H2 CrO4 20-30 <105 <0.005
    14 NaHCO3 >25 Room Temp. <0.005 35 FeCl3 10-40 <105 0.02-0.05
    15 NaHCO3 >25 100 <0.02 36 (HO3)C6H2COOH 100 <100 <0.005
    16 CuSO4 10-50 <105 <0.005 37 COOH(CH2) 2CH)(NH2) 100 <100 <0.005
    17 CuCl2 10-50 <105 <0.005 38 C6H6 100 <100 <0.005
    18 Cu (NO3)2 10-50 <105 <0.005 39 C6H5OH 100 <100 <0.005
    19 CH 3COOH ~100 <100 <0.005 40 NaNO3 10-50 <100 <0.005
    20 AlCl3 10 >200 >0.05 41 Na2SO4 20 <100 <0.005
    21 AlCl3 30 <105 <0.005 Attention: hydrofluoric acid, high-concentration phosphoric acid and high-concentration sodium hydroxide
    22 KAl (SO4)2 10-50 <105 <0.005